Para rubber sheets
Centaur Red
Colour
Red
Min. temperature
-30°C
Max. temperature
70°C
Specific gravity
1,1 grs/cm³
Hardness
45 Shore A +/- 5
Tensile strength
15 MPa
Elongation at break
600%
Abrasion
100 mm³
Article code
AB45110R
Features
Natural rubber quality with good mechanical properties, abrasion resistance, and low temperature flexibility.
Application
Very wide range of applications, conveyor systems, pumps etc.
Both sides smooth finish
| Thickness (mm) | Width (mm) | Length (mm) | Article code | Rolls per pallet |
|---|---|---|---|---|
| 1 | 1.400 | 20.000 | AB45110R 1/0 | On request |
| 1,5 | 1.400 | 15.000 |
AB45110R 1,5/0 |
On request |
| 2 | 1.400 | 10.000 | AB45110R 2/0 | 30 |
| 3 | 1.400 | 10.000 | AB45110R 3/0 | 25 |
| 3 | 2.000 | 10.000 | AB45110R 3/0 | 25 |
| 4 | 1.400 | 10.000 | AB45110R 4/0 | 16 |
| 4 | 2.000 | 10.000 | AB45110R 4/0 | 16 |
| 5 | 1.400 | 10.000 | AB45110R 5/0 | 16 |
| 5 | 1.500 | 10.000 | AB45110R 5/0 | 16 |
| 6 | 1.400 | 10.000 | AB45110R 6/0 | 12 |
| 6 | 2.000 | 10.000 | AB45110R 6/0 | 12 |
| 8 | 1.400 | 10.000 | AB45110R 8/0 | 9 |
| 8 | 2.000 | 10.000 | AB45110R 8/0 | 9 |
| 10 | 1.400 | 10.000 | AB45110R 10/0 | 6 |
| 10 | 1.400 | 20.000 | AB45110R 10/0 | 3 |
| 10 | 2.000 | 10.000 | AB45110R 10/0 | 6 |
| 10 | 2.000 | 20.000 | AB45110R 10/0 | 3 |
| 12 | 1.400 | 5.000 | AB45110R 12/0 | 6 |
| 12 | 2.000 | 10.000 | AB45110R 12/0 | 3 |
| 15 | 1.400 | 10.000 | AB45110R 15/0 | 3 |
| 15 | 2.000 | 10.000 | AB45110R 15/0 | 3 |
| 20 | 1.400 | 10.000 | AB45110R 20/0 | 3 |
| 20 | 2.000 | 10.000 | AB45110R 20/0 | 3 |
| 25 | 2.000 | 10.000 | AB45110R 25/0 | 2 |
Download datasheet
Zenith rubber Europe
High standard rubber solutions
- 95% of our product range is stored in our newest warehouse, located in central Europe.
- Storage capacity of 17.000 SQM in our new warehouse.
- Solarpowered by 5.000 panels.
- Our teams work with the Total Quality Management System, offering an efficient and reliable service experience.
- Zenith is globaly active, with offices in India, Europe and the Middle East.